Photocatalytic Purification and Treatment of Water and Air: Proceedings of the 1st International Conference on TiO2 Photocatalytic Purification and Treatment of Water and Air, London, Ontario, Canada, 8-13 November, 1992David F. Ollis, Hussain Al-Ekabi Elsevier, 1993 - 820 pagine Comprises the results of the first international conference examining the promise of the emerging area of photochemistry. It includes coverage of such areas as: comparison with other competitive technologies; and transfer of research results into development and application activities. |
Dall'interno del libro
Risultati 1-3 di 51
Pagina 445
... conducted using Mark A - 1 photo - reactor ( TiO2 loading density of 0.15 mg / cm2 ) at an air flow rate of 1 Lpm was equal to 3.3 . It should be noted that , even after taking NO into account , it was not possible to completely close ...
... conducted using Mark A - 1 photo - reactor ( TiO2 loading density of 0.15 mg / cm2 ) at an air flow rate of 1 Lpm was equal to 3.3 . It should be noted that , even after taking NO into account , it was not possible to completely close ...
Pagina 446
... conducted a series of experiments similar to those described above using Mark A - 2 reactor ( volume 12.8 L ) and a high air flow rate of 13.3 Lpm . NG decomposition products were collected normally for approximately 11⁄2 hours in a dry ...
... conducted a series of experiments similar to those described above using Mark A - 2 reactor ( volume 12.8 L ) and a high air flow rate of 13.3 Lpm . NG decomposition products were collected normally for approximately 11⁄2 hours in a dry ...
Pagina 691
... conducted in a 3ml cuvette photoreactor which was equipped with lamps emitting at two different wavelengths : 254 nm and 350 nm . The irradiated samples were made up of 4.5 * 10-5 M solution ( 12 ppm ) of PCP in water . Direct ...
... conducted in a 3ml cuvette photoreactor which was equipped with lamps emitting at two different wavelengths : 254 nm and 350 nm . The irradiated samples were made up of 4.5 * 10-5 M solution ( 12 ppm ) of PCP in water . Direct ...
Sommario
Conditions for an efficient photocatalytic activity of TiO2 particles | 1 |
Fundamental photoelectrochemistry of TiO and SrTiO applied to environmental | 19 |
Size quantization effects in photocatalysis | 39 |
Copyright | |
16 sezioni non visualizzate
Parole e frasi comuni
1993 Elsevier Science acid adsorbed adsorption Air D.F. Ollis Al-Ekabi Editors anatase B.V. All rights carbon Catal catalyst cell Chem chemical chlorine CO₂ concentration conduction band containing Cr(VI decrease degradation rate Degussa effect efficiency electron transfer energy experimental experiments Figure film flow rate flux formation holes hydroxyl radicals illumination increased initial intermediates irradiation kinetics lamp light intensity mg/L mineralization observed OH radicals Ollis and H oxidation oxygen Pelizzetti peroxide phenol photo-oxidation photocatalytic photocatalytic degradation photocatalytic oxidation Photocatalytic Purification Photochem photodegradation photodeposition photolysis photon photoreactor Phys pollutants potential presence Purification and Treatment quantum yield rate constant reaction rate reactive reactor recombination redox reduction rutile samples Science Publishers B.V. semiconductor Serpone solar species spectra studies substrate surfactant suspension Technol temperature TiO2 TiO2 particles TiO2 surface titanium dioxide Treatment of Water trichloroethylene UV light wastewater